TP430 SS Automotive Stainless Steel Tubing ASTM A268 For Boiler / Heat Exchanger

Typical applications for 430 grade include:

• Linings for dish washers
• Refrigerator cabinet panels
• Automotive trim
• Lashing Wire
• Element Supports
• Stove trim rings
• Fasteners
• Chimney Liners

Heat Treatment

• Solution Annealing – Heat to 815-845°C, hold for ½ hour per 25mm of thickness, slow furnace cool to 600°C and then quickly air cool. Slow cooling from 540-400°C will cause embrittlement.
• Sub-Critical anneal – Heat to 760-815°C and then air cool or water quench.
• This grade is not hardenable by thermal treatment.

Welding

• Pre-heat at 150-200°C if welding is necessary.
• Embrittlement in the weld metal and heat affected zone can be relieved by a post-weld anneal at 790-815°C
• Grain refinement will not occur.

Machining

• Easier to machine than the standard austenitic grades such as 304.
• Still a tendency for galling and pick-up on the cutting tool.
• Bars that have been lightly drawn are easier to machine than those in the annealed condition.
• Grade 430F, the free machining version of 430, is very much easier to machine.

Fabrication

• Lower work hardening rate makes bending and forming somewhat easier than for grade 304
• Lower ductility restricts very severe operations.
• Severe bends should be made with the bend axis at right angles to the rolling direction.
• Severe cold heading of 430 wire is possible.