Product Details:
Payment & Shipping Terms:
|
| Product Name: | Copper Nickel Tube | Standard: | ASTM B111/ASME SB111 |
|---|---|---|---|
| Tube Shape: | U Tube | Materials No.: | C68700 |
| Manufacturing: | Cold Drawn/Seamless | Surface: | O61 Annealed |
| OD: | 1/2'' - 2'' | WT: | 0.035'' - 0.083'' |
| Package: | Wooden Case | Application: | Heat Exchanger |
| High Light: | u bend tube,aluminium extruded finned tubes |
||
ASME SB111 C68700 Aluminum Brass Seamless Tube u tube heat exchanger
This specification covers U-bend seamless condenser, evaporator, and heat exchanger tubes of copper and copper alloys up to 2 in., inclusive, in diameter. Tubes for this application are normally made from the following copper or copper alloys:
Copper Alloy Tube----Aluminum Brass Tube
Aluminum Brass Tube is a copper zinc alloy containing aluminum and small amount of arseric which is added as an inhibitor against dezincification. Inhibited Aluminum Brass resists the action of high velocity salt and brackish water and is commonly used for condenser tube.
The outstanding characteristic of Aluminum Brass is th high resistance to impringement attack.
Aluminum Brass tubes are highly accepted and one of the extensively used material for various industrial applications.
Product Range
• Outside diameter : 5.0 mm(min) ~ 65 mm(max)
• Wall thickness : 0.5mm(Min.)
• Length : 27,000mm(Max.)
• Product capacity per month : 500 M.T.
• U-bend tube (smallest bending radius ≥ 2 x tube O.D.)
Application :
Steam Ejector, Intor and After Condensers, Grand steam condensers, Feed Water Evaporators for Petrochemical, Ship-building, Power plants and Desalination plants etc.
Chemical composition
| Standard | Class | Chemical composion(%) | Related standards | ||||||||||||||
| Cu | Zn | Pb | Fe | P | Sn | Ni | Mn | Al | As | Other | KS | JIS | ASTM | BS | DIN | ||
| ASTM | 1 | 76.0-79.0 | Rem. | 0.07 Max. | 0.06 Max. | 1.8-2.5 | 0.02-0.10 | D5301 C6870 | H3300 C6870 | B111 C68700 | 2871 CZ110 | 1785 CuZn20Al | |||||
| 2 | 76.0-79.0 | Rem. | 0.05 Max. | 0.05 Max. | 1.8-2.5 | 0.02-0.06 | Si 0.2-0.5 | C6871 | C6871 | C68700 | 2871 CZ110 | CuZn20Al | |||||
| 3 | 76.0-79.0 | Rem. | 0.07 Max. | 0.06 Max. | 0.20 - 1.0 | 0.20-Max. | 1.8-2.5 | 0.02-0.06 | Cr0.10 Max. | C6872 | C6872 | C68700 | 2871 CZ110 | CuZn20Al | |||
Mechanical properties
| Standard | Temper | Designation | Tensile test | Hardness test | |||||
| Outside diameter(mm) | Thickness (mm) | Tensile strength min ksi | Elongation in 2in., min% | Yield strength min ksi | Rockwell hardness | ||||
| HR30T | HR15T | ||||||||
| ASTM | O61 | C68700 | 5-50 | 0.8-0.10 | 50 | - | 18 | - | - |
| JIS | O61 | C6871T-O | 50-250 | 0.8-0.10 | 36Min. | 40Min. | 13Min. | - | - |
| C6872T-O, C687TS-O | 50-250 | 0.8-0.10 | 36Min. | 40Min. | 13Min. | - |
- |
||
Additional Testing
We are equipped to carry out heat treatment of bends plus a minimum 150mm of leg.
Heat Treatment Equipment
Chemical Composition
|
| Materials - U-Bent Tube | |
|---|---|
| Carbon Steel | SA 179 / A 179 |
| Carbon Steel | SA 210 / A 210 |
| Carbon Steel | SA 334 / A 334 |
| Stainless Steel | SA 213 / A 213 |
| SA249 / A249 | |
| SA268 / A268 | |
| SA688 / A688 | |
| Duplex Stainless Steel | SA 789 / A 789 |
| Copper & Cu Alloys | SB 111 / B 111 |
| Titanium & Ti Alloys | SB 338 / B 338 |
| For different materials please contact our sales department. | |
Mechanical Properties
| Physical Properties | Conditions | ||
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 8.8-8.94 | 25 | |
| Poisson's Ratio | 0.34 | 25 | |
| Elastic Modulus (GPa) | 117 | 25 | |
| Tensile Strength (Mpa) | 414 | 25 | Tube |
| Yield Strength(Mpa) | 186 | ||
| Elongation (%) | 55 | ||
| Reduction in Area (%) | |||