Product Details:
Payment & Shipping Terms:
|
| Outer Diameter: | 400mm | Tube Standrad: | ISO1127 |
|---|---|---|---|
| Material Grade: | 1.4301, 1.4307, 1.4404 | Outside Dia.: | 15.88MM-114.3MM |
| Wall Thick: | 0.50MM - 3.05MM | Tolerance: | D4/T3 |
| Surface Finish: | Annealed & Pickled, Bright Annealed | Shape: | Round |
| Package: | Wooden Case | Application: | Buildings,industry |
| High Light: | Oval Stainless Steel Welded Pipe,Decorative 316 Stainless Steel Round Tube,Handrail Welded Steel Pipe |
||
Decorative Welded Stainless Steel Inox 316 Oval Shape Tube For Handrail / Window / Door
|
Product Name
|
ss 201 304 316 304l 316l 76.2mm diameter 1.5mm thickness welded polished stainless steel tube price per length
|
|
Standard
|
316L 201 304 316 202 2 inch diameter stainless steel pipe weight per piece SUS ANSI ASTM EN A249 DIN Austenitic ASME AISI JIS A789
|
|
Out Diameter
|
6-1024mm
|
|
Thickness
|
0.3-68mm
|
|
Length
|
1-6m or as customers required
|
|
round pipe/tube o.d. (mm)
|
8, 9.5 , 12.7 , 15.9 , 17 , 18 , 19. 1 , 20 , 21 , 22.2 , 23 , 25.4 , 28 , 31.8 , 33, 35, 36, 38.1 , 40 , 41.8 , 42 , 45, 48 , 50 , 50.8 , 56 , 57 , 60, 63.5 , 76.2 , 80 , 89 , 101.6 , 108 , 114 , 127 , 133 , 141 , 159 , 168, 219, etc.
|
|
rectangular/square
pipe/tube (mm) |
10*10 , 12*12 , 15*15 , 18*18 , 19 * 19 , 20*10 , 20*20 , 22* 22 , 23* 11 , 23 *23 , 24* 12 , 24*24 ,25*13 , 25*25 , 28*28 , 30*15 , 30*30 , 30*60 , 36*23 , 36*36 , 38*25 , 38*38 , 40*10 , 40*20 , 40*40 ,45*75 , 48*23 , 48*48 , 50*25 , 50*50 , 55*13 , 60*40 , 60*60 , 70*30 , 73*43 , 80*40 , 80*60 , 80*80 , 95*45 , 100*40 ,100*50 ,100*100 , 120*60 , 150*100 , 150*150,etc.
|
|
shape
|
round/ square/ rectangular/ oval/ specia section
|
|
Application
|
industry, chemical, machinery, architecture, decoration, etc.
|
Chemical Composition
| Grade | Chemical Composition % | ||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | N | |
| 1Cr17Mn6Ni5N (201) | ≤0.15 | 16.00-8.00 | 3.50-5.50 | 5.50-7.50 | ≤0.06 | ≤0.03 | ≤1.00 | ≤0.25 | |
| 1Cr18Mn8Ni5N (202) | ≤0.15 | 17.0019.00 | 4.00-6.00 | 5.50-7.50 | ≤0.06 | ≤0.03 | ≤1.00 | ≤0.25 | |
|
0Cr18Ni9 (304) |
≤0.07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0.035 | ≤0.03 | ≤1.0 | ||
|
00Cr18Ni10 (304L) |
≤0.03 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0.035 | ≤0.03 | ≤1.0 | ||
| 0Cr17Ni12Mo2 (316) | ≤0.08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0.035 | ≤0.03 | 2.003.00 | ≤1.0 | |
| 0Cr17Ni14Mo2 (316L) | ≤0.03 | 16.00-18.00 | 12.00-15.00 | ≤2.00 | ≤0.035 | ≤0.030 | 2.00-3.00 | ≤1.0 | |
Corrosion Resistance
Grade 316 has excellent corrosion resistance when exposed to a range of corrosive environments and media. It is usually regarded as “marine grade” stainless steel but is not resistant to warm sea water. Warm chloride environments can cause pitting and crevice corrosion. Grade 316 is also subject to stress corrosion cracking above around 60°C.
Heat Resistance
316 has good resistance to oxidation in intermittent service to 870°C and in continuous service to 925°C. However, continuous use at 425-860°C is not recommended if corrosion resistance in water is required. In this instance 316L is recommended due to its resistance to carbide precipitation.
Where high strength is required at temperatures above 500°C, grade 316H is recommended.
Fabrication
Fabrication of all stainless steels should be done only with tools dedicated to stainless steel materials. Tooling and work surfaces must be thoroughly cleaned before use. These precautions are necessary to avoid cross contamination of stainless steel by easily corroded metals that may discolour the surface of the fabricated product.
| Chemical Element | % Present |
|---|---|
| Carbon (C) | 0.0 - 0.03 |
| Chromium (Cr) | 16.50 - 18.50 |
| Molybdenum (Mo) | 2.00 - 2.50 |
| Silicon (Si) | 0.0 - 1.00 |
| Phosphorous (P) | 0.0 - 0.05 |
| Sulphur (S) | 0.0 - 0.03 |
| Nickel (Ni) | 10.00 - 13.00 |
| Manganese (Mn) | 0.0 - 2.00 |
| Nitrogen (N) | 0.0 - 0.11 |
| Iron (Fe) | Balance |
| Physical Property | Value |
|---|---|
| Density | 8.0 g/cm³ |
| Melting Point | 1400 °C |
| Thermal Expansion | 15.9 x10^-6 /K |
| Modulus of Elasticity | 193 GPa |
| Thermal Conductivity | 16.3 W/m.K |
| Electrical Resistivity | 0.074 x10^-6 Ω .m |