ASTM B163 ASME SB167 N06601 Inconel 601 Nickel Alloy Seamless Tubing
ASTM B163 B167 ASME SB163 SB167 N06601 Inconel 601 Nickel Alloy Seamless Tubes Tubing Pipes DIN 17552 2.4851 is a nickel-chromium alloy used for applications that require resistance to corrosion and heat. This nickel alloy stands out due to its resistance to high temperature oxidation, remaining highly resistant to oxidation through 2200° F. Alloy 601 develops a tightly adherent oxide scale which resists spalling even under conditions of severe thermal cycling. This nickel alloy has good high temperature strength, and retains its ductility after long service exposure.
ASTM B163 B167 ASME SB163 SB167 N06601 Inconel 601 Nickel Alloy Seamless Tubes Tubing Pipes has good resistance to aqueous corrosion, high mechanical strength, and is readily formed, machined and welded . Inconel 601 2.4851 properties make it a material of broad utility in fields like thermal processing, chemical processing, pollution control, aerospace, and power generation. However, alloy 601 2.4851 is not suggested for use in strongly reducing, sulfur bearing environments.
Inconel 601 is a nickel-chromium alloy, that is highly resistant to oxidation through 2200°F. 601 alloy develops a tightly adherent oxide scale which resists spalling even under severe thermal cycling. The alloy has good high temperature strength, and retains its ductility after long service exposure. 601 alloy has good hot corrosion resistance under oxidizing conditions. 601 alloy is not suggested for use in strongly reducing, sulfur bearing environments.
The most important property of Inconel 601 is resistance to oxidation at very high temperatures up to 1250C. Even under severe conditions such as, cyclical heating and cooling. This is possible due to Inconel 601 having a tightly adherent oxide layer which is resistant against spalling.
Resistance to carburization is good, also resistant to carbon nitriding conditions.
Due to high chromium and some aluminum content, good resistance in oxidizing sulfur bearing atmospheres at elevated temperatures is demonstrated.
|Nickuel||58.0 - 63.0|
|Cromium||21.0 - 15.0|
|Alumnium||1.0 - 1.7|
Trays, baskets and fixtures used in various heat treatments such as carburizing and carbon nitriding.
Refractory anchors, strand annealing and radiant tubes, high velocity gas burners, wire mesh belts etc.
Insulating cans in ammonia reformers and catalyst support grids used in nitric acid production.
Thermal reactors in exhaust system of petrol engines.
Fabricated combustion chambers.
Tube supports and ash trays in the power generation industry.