Product Details:
Payment & Shipping Terms:
|
| Material Grade: | 400 Series | Size Range: | 19.05mm 25.4mm |
|---|---|---|---|
| WT: | 2.11mm 1.65mm | Length: | 6096mm |
| Specification: | ASTM A268, ASME SA268 | Finishing Options: | Pickling, Polishing, Custom Cutting |
| Test Certificate: | EN10204 3.1 | Packaging: | Wooden Box, Bundled, Export Packaging Available |
| Application: | Boiler,Heat Exchanger | Shape: | Round |
| Product Name: | TP410 Ferritic Stainless Steel Tube | ||
| Highlight: | seamless stainless steel tubing,rolled stainless steel tubing |
||
400 Series Stainless Steel,TP410 ferritic Stainless Steel Tube for boiler
The 400 series group of stainless steels has an 11 percent chromium and 1-percent manganese increase, above the 300 series group. The 400 series is susceptible to rust and corrosion under some conditions. Heat-treating will harden the 400 series. The 400 series of stainless steels have higher carbon content, giving it a martensitic crystalline structure.This provides high strength and high wear resistance. Martensitic stainless steels aren’t as corrosion resistant as the austenitic types.
Typical Manufacturing Specifications:
ASTM A268
ASME SA268
- Harding by heat treatment
- High hardness with good ductility
- Good corrosion resistance capability
- Good wear corrosion resistance
- High cold-deformation property
Available Tube Product Forms:
Straight.
Coiled.
Typical Applications:
Used for parts requiring a combination of good strength and toughness, plus reasonable corrosion resistance. Typical applications are: Bolts, Bushings, Fasteners, Gas Turbine Parts, Mine Equipment, Pump Parts, Petrochemical Equipment, Steam Turbine Parts, Studs, Valve Parts etc.
Material magnetic in all conditions.
AISI Type 410 is a martensitic stainless steel that provides high strength and hardness with moderate corrosion resistance. A wide range of properties can be developed with different heat treatments, with ultimate tensile strengths ranging from 500 to 1400 MPa. It is magnetic in both the annealed and hardened conditions. High carbon content results in the formation of chromium carbide compounds, providing excellent wear resistance and edge retention when hardened. Additionally, this grade provides excellent high temperature oxidation and scaling resistance, yet is economical due to the low alloy content. Thermal conductivity is improved and thermal expansion reduced relative to austentic stainless grades.
Composition:
| Item Code: | TP410 |
| Tube OD.: | 1/4'' - 2'' |
| Wall: | 0.028'' - 0.120'' |
| Length: | 20FT |
| Material: | 410 |
| Standard: | ASTM A268 ASME SA268 |
| Finish: | Annealed & Pickled. |
| Type: | Seamless Cold Drawn |
| Certification: | ISO9001:2015 |
| Mill Test Certificate: | EN10204 3.1 |
| Packing: |
Sleeved, Wooden Boxed |
Quality Assurance:
Spezilla's seamless bright annealed stainless steel tubes are produced acc. to the following process and inspection to assure our quality:
1. Chemical Composition Analysis Test With 100% PMI.
2. Solution Annealing / Bright Annealed.
3. 100% Hydrostatic Test and 100% Eddy Current Test
4. Mechanical Tests includes Tension Test, Flattening Test, Flaring Test, Hardness Test.
5. Impact Test subject to Standard request.
6. Grain Size Test and Intergranular Corrosion Test.
7. Visual Test and Endoscope Test for Surface Quality Test
Grade 410S is a ferritic stainless steel that is a lowcarbon variation of ferritic type 410 stainless steel. Due to the lower level of carbon and the addition oftitanium and/or columbium, this alloy minimizesaustenite formation at higher temperatures. This alsoprevents hardening and prevents cracking whenwelding.
| 5% Test Solution at 120°F (49°C) |
Corrosion Rate in Mils per Year and Millimeters per Year (mm/a) | ||||||
|---|---|---|---|---|---|---|---|
| Alloy 409 | Alloy 410S | Alloy 420 | Alloy 425 Mod | Alloy 440A | Alloy 430 | ||
| Acetic Acid | 0.88 (0.022) |
0.079 (0.002) |
1.11 (0.028) |
4.79 (0.122) |
2.31 (0.0586) |
0.025 (0.0006) |
|
| Phosphoric Acid | 0.59 (0.002) |
0.062 (0.002) |
0.068 (0.002) |
0.593 (0.015) |
0.350 (0.009) |
0.029 (0.001) |
|
ASTM A268 Tp410 tube composition:
| Grade: | TP405 | TP410 | TP249 | TP430 | TP443 | TP446-1 | TP446-2 | … | TP409 |
| UNS | S40500 | S41000 | S42900 | S43000 | S44300 | S44600 | S44600 | S40800 | S40900 |
| C, max | 0.08 | 0.15 | 0.12 | 0.12 | 0.20 | 0.20 | 0.12 | 0.08 | 0.08 |
| Mn,max | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.50 | 1.50 | 1.00 | 1.00 |
| P, max | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | 0.045 | 0.045 |
| S, max | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.045 | 0.045 |
| Si, max | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 | 1.00 |
| Ni | 0.50max | … | … | … | 0.75max | 0.75max | 0.50max | 0.80max | 0.50max |
| Cr | 11.5-14.5 | 11.5-13.5 | 14.0-16.0 | 16.0-18.0 | 18.0-23.0 | 23.0-27.0 | 23.0-27.0 | 11.5-13.0 | 10.5-11.7 |
| Mo | … | … | … | … | … | … | … | … | … |
| Al | 0.10-0.30 | … | … | … | … | … | … | … | … |
| Cu | … | … | … | … | 0.90-1.25 | … | … | … | … |
| N | … | … | … | … | … | 0.25 | 0.25 | 12xCmin | 6xCmin |
| Ti | … | … | … | … | … | … | … | 1.10max | 0.75max |
| Chemical Composition | |||||||||||
| Min. % | Max % | ||||||||||
| Carbon | 0.09 | 0.15 | |||||||||
| Silicon | 0 | 1.00 | |||||||||
| Manganese | 0 | 1.00 | |||||||||
| *Nickel | 0 | 1.00 | |||||||||
| Chromium | 11.50 | 13.50 | |||||||||
| Phosphorous | 0 | 0.04 | |||||||||
| Sulphur | 0 | 0.03 | |||||||||
| *Nickel additional option | |||||||||||