|Material Grade:||TP410 410S||Size Range:||25.4mm 38.1mm|
|Specification:||ASTM A268, ASME SA268||Finishing Options:||Pickling, Polishing, Custom Cutting|
|Test Certificate:||EN10204 3.1||Packaging:||Wooden Box, Bundled, Export Packaging Available|
|Product Name:||TP410 Ferritic Stainless Steel Tube|
seamless stainless steel tubing,
high pressure stainless steel pipe
TP410 410S Ferritic Stainless Steel Tube,ASTM A268 Ferritic heat exchanger tube
Quenching and tempering can harden this grade of ASTM 410 Tubes. Meanwhile, our Stainless Steel Workstoff Nr. 1.4006 Pipes & Tubes are available in different sizes, specification & thickness as per the clients’ customized requirements.
This specification covers a number of grades of nominal-wall-thickness, stainless steel tubing for general corrosion-resisting and high-temperature service. Most of these grades are commonly known as the "straight-chromium" types and are characterized by being ferromagnetic. Two of these grades, TP410 and UNS S 41500 in the specification, are amenable to hardening by heat treatment, and the high-chromium, ferritic alloys are sensitive to notch-brittleness on slow cooling to ordinary temperatures. These features should be recognized in the use of these materials. Grade TP439 is used primarily for hot-water tank service and does not require post-weld heat treatment to prevent attack of the heat affected zone.
SS TP410S Seamless Tubes is mainly useful for quenching racks, annealing boxes, oxidation-resistant panels and other soaring-temp units. Alloy 410S Seamless Tubes has an extensive requirement for heat transfer process machinery like boilers, super heaters, heat exchangers and condensers.
TP410 is a typical martensitic chromium-alloy steel grade. It does not have the nickel content and owns the following characteristic:
- Harding by heat treatment
- High hardness with good ductility
- Good corrosion resistance capability
- Good wear corrosion resistance
- High cold-deformation property
410S Stainless Steel Seamless Tubes Specification :
|Specifications||ASTM A268 / SA 268|
|Dimensions||ASTM, ASME and API|
|Size||1/4" (6.25mm) to 8" (203mm), WT 0.02" (0.5mm) to 0.5"(12mm)|
|Schedule||SCH20, SCH30, SCH40, STD, SCH80, XS, SCH60, SCH80, SCH120, SCH140, SCH160, XXS|
|Specialized in||Large Diameter Size|
|Length||Single Random, Double Random & Cut Length.|
|Form||Round, Square, Rectangular, Hydraulic Etc|
|End||Plain End, Beveled End, Treaded|
Spezilla's seamless bright annealed stainless steel tubes are produced acc. to the following process and inspection to assure our quality:
1. Chemical Composition Analysis Test With 100% PMI.
2. Solution Annealing / Bright Annealed.
3. 100% Hydrostatic Test and 100% Eddy Current Test
4. Mechanical Tests includes Tension Test, Flattening Test, Flaring Test, Hardness Test.
5. Impact Test subject to Standard request.
6. Grain Size Test and Intergranular Corrosion Test.
7. Visual Test and Endoscope Test for Surface Quality Test
Available Tube Product Forms:
Used for parts requiring a combination of good strength and toughness, plus reasonable corrosion resistance. Typical applications are: Bolts, Bushings, Fasteners, Gas Turbine Parts, Mine Equipment, Pump Parts, Petrochemical Equipment, Steam Turbine Parts, Studs, Valve Parts etc.
Material magnetic in all conditions.
Typical Manufacturing Specifications:
Also individual customer specifications.
TP410 material does not have the nickel content and has a relative low material cost. Besides, it can replace some austenitic steel grades under some mild corrosion condition.
ASTM A268 Tp410 tube composition:
|Tube OD.:||1/4'' - 2''|
|Wall:||0.028'' - 0.120''|
|Standard:||ASTM A268 ASME SA268|
|Finish:||Annealed & Pickled.|
|Type:||Seamless Cold Drawn|
|Mill Test Certificate:||EN10204 3.1|
|Packing:||Sleeved, Wooden Boxed|
|Min. %||Max %|
|*Nickel additional option|
|Typical Mechanical Properties At Room Temperature - Hardened By Oil Quench at 1010oC and Tempered as Indicated|
|Tensile Strengt Mpa||1350||1295||1300||690||830||730|
|0.2% Yield Strength Mpa||1095||1070||1020||915||725||630|
|Elongation in 50mm %||17||17||18||19||20||21|
|Impact Charpy J||76||66||*38||*33||52||95|